ASTM D3012-2007 用炉内样品旋转器测定丙烯塑料的热氧化稳定性的标准试验方法
【英文标准名称】: Standard Test Method for Thermal-Oxidative Stability of Polypropylene Using a Specimen Rotator Within an Oven 【原文标准名称】: 用炉内样品旋转器测定丙烯塑料的热氧化稳定性的标准试验方法 【标准号】: ASTM D3012-2007 【标准状态】: 现行 【国别】: 【发布日期】: 2007 【实施或试行日期】: 【发布单位】: 美国材料与试验协会(US-ASTM)【起草单位】: D20.15【标准类型】: (Test Method)【标准水平】: ()【中文主题词】: 热学;氧化;塑料;丙烯;耐力;稳定性;测试【英文主题词】: aging; biaxial rotator; polypropylene; thermal aging; thermal oxidative stability【摘要】: Under the severe conditions of this test method, the specimens undergo degradation at a rate that is dependent upon the thermal endurance of the polypropylene material under examination. The thermal level of this test method is considered sufficiently severe to cause failure of commercial grades of heat-stable polypropylene within a reasonable period of time. If desired, lower temperatures can be applied to estimate the performance of polypropylene materials with lower heat stability. The technique of specimen rotation described in this test method provides an estimate of the life-temperature relationship of polypropylene. If this test method is conducted at different temperatures on the same material, a more reliable estimate of the life-temperature relationship of polypropylene is determined. This test method can be conducted at several temperatures and the data interpreted through use of the Arrhenius relation, by plotting the logarithms of times to failure against the reciprocals of the temperatures in kelvins (K). Temperatures in the range from 100 to 150x00B0;C, with intervals of 10x00B0;C, are suggested for this purpose. The stability as determined under the prescribed test method is not directly related to the suitability of the compound for a use where different conditions prevail. The specimen rotation technique of thermal aging increases the probability that all specimens will be exposed similarly and that the effect of temperature gradients in an oven will be minimized.1.1 This test method provides a means for estimating the resistance of polypropylene, in molded form, to accelerated aging by heat in the presence of air using a forced draft oven.1.2 The stability determined by this test method is not directly related to the suitability of the material for use when different environmental conditions prevail and shall not be used to predict performance.Note 1The specified thermal levels in this test method are considered sufficiently severe to cause failure of commercial grades of heat-stable polypropylene within a reasonable period of time. If desired, lower temperatures can be applied to estimate the performance of polypropylene with lower heat stabilities.1.3 The values stated in SI units are to be regarded as the standard. The values in brackets are for information only. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.Note 2This test method and ISO 4577-1983 are technically similar but different in preparation of test specimens, thickness of test specimen, measurement of the number of air flow changes in the ovens, and the number of air changes per hour required.1.4 The purpose of this appendix is to provide a secondary method for determining the number of air exchanges that occur within the forced draft oven used for measurement of thermal oxidative stability.【中国标准分类号】: G31【国际标准分类号】: 83_080_20【页数】: 6P.;A4【正文语种】:
ENENENENEN:):):):):):):):):):):):):):) 最近正在看这个标准，可是没看到又可以洗啊在的附件啊？求分享
页:
[1]